Metal
Inconel 625 annealed sheet, <=6.3 mm (MIL-HDBK-5H)
Historical public-release annealed-sheet reference conservatively combined through 6.3 mm.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 8442 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 813.581 | MPa |
| Tensile yield strength, L | 365.422 | MPa |
| Ultimate tensile strength, LT | 820.476 | MPa |
| Tensile yield strength, LT | 372.317 | MPa |
| Compressive yield strength, L | 379.212 | MPa |
| Compressive yield strength, LT | 386.106 | MPa |
| Ultimate shear strength | 544.686 | MPa |
| Elongation, LT | 30 | % |
| Young's modulus | 205.464 | GPa |
| Compression modulus | 205.464 | GPa |
| Shear modulus | 81.358 | GPa |
| Poisson's ratio | 0.28 | - |
Units
Condition
- Condition
- Inconel 625; annealed sheet; <=6.3 mm
- Temper
- annealed
- Heat treatment
- annealed at 1700-1900 degF for time commensurate with thickness per handbook section 6.3.3
- Product form
- sheet
- Thickness / diameter range
- <=0.248 in (6.3 mm), within the <=0.250 in table columns
- Test direction
- L and LT; lower listed value across applicable thickness columns
- Processing route
- wrought solid-solution-strengthened nickel-alloy sheet
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.