Metal
Ti-10V-2Fe-3Al STA die forging, <76.2 mm (MIL-HDBK-5H)
Historical public-release S-basis conventional die-forging reference.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 4650 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 1192.793 | MPa |
| Tensile yield strength, L | 1103.161 | MPa |
| Ultimate tensile strength, LT | 1192.793 | MPa |
| Tensile yield strength, LT | 1103.161 | MPa |
| Compressive yield strength, L | 1158.319 | MPa |
| Compressive yield strength, LT | 1144.53 | MPa |
| Ultimate shear strength | 668.791 | MPa |
| Elongation, L | 4 | % |
| Elongation, LT | 4 | % |
| Ultimate tensile strength, ST | 1192.793 | MPa |
| Tensile yield strength, ST | 1103.161 | MPa |
| Compressive yield strength, ST | 1144.53 | MPa |
| Elongation, ST | 4 | % |
| Young's modulus | 109.627 | GPa |
| Compression modulus | 112.385 | GPa |
Units
Condition
- Condition
- Ti-10V-2Fe-3Al; solution treated and aged; conventional die forging; <76.2 mm
- Temper
- solution treated and aged (900-950 degF)
- Heat treatment
- solution treated below beta transus, water quenched and aged 8 hours at 900-950 degF
- Product form
- conventional die forging
- Thickness / diameter range
- <3.000 in (76.2 mm)
- Test direction
- L, LT and ST subject to the source-table transverse-dimension footnote
- Processing route
- alpha-beta processed near-beta titanium-alloy die forging
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI